Characteristics of high-performance multi-function tile
1 Anti-slip effect
Slip-resistant special glaze achieved a high CSR and CSR-B score.
|Test Requirement||Test slip resistance|
|Test Method||Slip testing machine by OY-PSM|
|(Inclusion : water + powder for test 1-4 )|
|Slip resistance Result||C.S.R-B 1.48|
|C.S.R. Rate||C.S.R 0.61|
2 Antifouling effect
The mineral glass closes the fine pores of the tile surface to prevent dirt entering.
3 Anti-scratch effect
The mineral glass on the surface has Mohs Hardness 8(same as Topaz, while Diamond has 10) will have very little scratches.
4 High wear resistance
The glaze satisfies CLASS IV(for heavy traffic) in European Standard, and best suitable for public space floors.
|Chemical Resistance||EN122||class AA|
|Abrasion strength (Morse strength)||EN101||8|
|Water absorption||JIS A 5209||0.02%|
|Wear resistance||EN154||class Ⅳ|
|Abrasion loss||JIS A 5209||0.03g|
|Bending fracture load||JIS A 5209||306N/cm×8|
CT processing ( by custom order)
The characteristic of charge transfer type oxidation-reduction catalyst is excellent in self-cleaning and durability.
• Anti-bacteria, along with the deodorant effect can be expected. It has the effect of cleaning the surrounding environment, such as to decompose the NOx and formaldehyde in the air that touches the CT catalyst layer.
|Deodorant effect||The rate of decrease after 24 hours after|
Deodorant effect will be recognized at 70% or more.
|Antibacterial performance||Escherichia coil||Staphylococcus aureus|
|Decrease percent bacteria||99.90%||99.90%|
|Antibacterial activity value||7.5||4.7|
Antibacterial performance is approved antibacterial effect at 2.0 or higher
• The oxidation-reduction reaction decomposes substances that cause stains and dirt. Even if the dirt is on the surface, you can wash it away easily with water due to the high water-repellent effect.
• Regardless of the brightness of the light, it can decompose the dirt and keep the self-cleaning function. The environment adaptive tile does not require any substance of environmental concern.
• After CT catalyst mixed with glaze and fired at high temperature of 1250 or more, the surface hardness can be achieved and be expected self-cleaning effect for a long time.
RGS-150 / R-401
RGS-150 / R-402
RGS-150 / R-403
RGS-150 / R-404
RGS-150 / R-405
RGS-150 / R-406
RGS-150 / R-407
RGS-150 / R-408
Thickness : 9mm (0.35″)